Monomeric PVC soft film
Available in white with a glossy or matte surface, or transparent with a glossy or matte surface.

Release Paper
Silicone-coated paper, 135 g/m².

Adhesive
Permanent polyacrylate, transparent.

Area of Use
Designed for brilliant and colorful short- and medium-term outdoor applications.

Printing Method
Compatible with inkjet printing using solvent-based inks, UV, or latex inks.

Certificates:
• ISO 9001
• ISO 14001
• ISO 50001
• GMP - flame retardant, limited smoke, no dripping.

Technical Data
• Thickness (without paper and adhesive): 80 microns.
• Dimensional Stability (FINAT TM 14): Adhered to steel, no shrinkage in cross direction, maximum 0.4 mm in length.
• Temperature Resistance: Adhered to aluminum, from -40° C to +80° C, no variation.
• Water Resistance: Adhered to aluminum, after 48 hours at 23° C, no variation.
• Adhesive Power (FINAT TM 1, after 24 hours, stainless steel): 16 N/25 mm.
• Tensile Strength (DIN EN ISO 527): Along: minimum 19 MPa, Across: minimum 19 MPa.
• Elongation at Break (DIN EN ISO 527): Along: minimum 130%, Across: minimum 150%.
• Shelf Life: 2 years in original packaging at 20° C and 50% relative humidity.
• Minimum Application Temperature: >+10° C.
• Service Life by Specialist Application: Under vertical outdoor exposure in normal Central European climate: 4 years (unprinted).

Note
After printing, ensure the ink is thoroughly dry before applying laminate. Surfaces for material application must be clean, free from dust, grease, and any contaminants that could affect adhesion. Freshly lacquered or painted surfaces should dry for at least three weeks to fully cure. Compatibility of selected lacquers and paints should be tested by the user prior to application.

Release Paper:
High-quality release paper, which ensures easy handling and application. The release paper protects the film’s adhesive surface, allowing for precise placement and preventing contamination during storage and installation.

Adhesive:
Our polyurethane films are equipped with advanced adhesives that provide strong bonding to various substrates. The adhesive is designed to offer optimal tack and peel strength, ensuring the film remains securely in place even under challenging conditions. It also facilitates clean removal without leaving residue.

Area of Use:
Polyurethane films are incredibly versatile and find applications across multiple industries, including automotive, medical, textile, and electronics. They are ideal for protective coverings, laminations, and surface coatings where flexibility, durability, and resistance to environmental factors are crucial.

Certificates:
• ISO 9001
• ISO 14001
• ISO 50001
• GMP - flame retardant, limited smoke, no dripping.

Technical Data:
Our polyurethane films are characterized by their exceptional physical properties, including high tensile strength, elongation, and abrasion resistance. They are available in various thicknesses and grades, tailored to meet specific application requirements. The films also boast excellent chemical resistance and remain stable across a broad temperature range, ensuring consistent performance in diverse environments.

Polymeric PVC Film:
Available in white and transparent with a glossy or matte surface.

Release Paper:
Double-sided PE coated paper, siliconized on one side, 143 g/m².

Adhesive:
Solvent polyacrylate, repositionable with permanent final adhesion, grey or transparent.

Area of Use:
Ideal for long-term outdoor displays requiring high brilliance and durability, such as vehicle lettering.

Printing Method:
Suitable for inkjet printing with solvent-based inks, UV, or latex inks.

Certificates:
• ISO 9001
• ISO 14001
• ISO 50001
• GMP - flame retardant, limited smoke, no dripping.

Technical Data
• Thickness (without paper and adhesive): 70 microns.
• Dimensional Stability (FINAT TM 14): Adhered to steel, no shrinkage in cross direction, max 0.2 mm in length.
• Temperature Resistance: Adhered to aluminum, -50° C to +90° C (short-term, max 24h, at +100° C), no variation.
• Sea Water Resistance (DIN 50021): Adhered to aluminum, after 100h/23° C, no variation.
• Resistance to Solvents and Chemicals: At room temperature, 72h after adhesion to aluminum, short-term resistant to most oils and greases, fuels, aliphatic solvents, weak acids, salts, and alkalis.
• Adhesive Power (FINAT TM 1, after 24h, stainless steel): 18 N/25 mm.
• Tensile Strength (DIN EN ISO 527): Along: > 19 MPa, Across: > 19 MPa.
• Elongation at Break (DIN EN ISO 527): Along: > 130%, Across: > 150%.
• Shelf Life: 2 years in original packaging at 20° C and 50% relative humidity.
• Application Temperature: >+8° C.
• Maximum Service Life by Specialist Application: Applies for vertical outdoor exposure: 7 years (unprinted).